معلومات المنتج

- Highly esthetic 4:1 composite material for provisional crowns and bridges inlays, onlays and veneers. - High fracture resistance also in very thin layer such as edges of crowns or thin veneers. - Very aesthetic appearance with high color stability and natural fluorescence. - Material of the latest generation with mixing ratio 4:1. - Very high mechanical durability and excellent elasticity. - Optimal for long bridges with high durability. - Excellent fit due to minimal polymerization shrinkage. - High abrasion resistance. - Excellent polishability. - Safe and quick handling with a self-mixing cartridge system. - Direct chairside application due to low curing temperature. - Final preparation after only 5 min. - Working time at 23 ° C / 73 °F 0:50 min. - Shore- D- hardness 75. - Barcol- hardness 36. - Flexural strength 88 MPa. - Compressive strength 304 MPa. - Diametral tensile strength 44 MPa. - Elasticity Modulus 2,7 GPa. Pack contains: - 1 x 50 ml cartridge. - 10 x mix tips. **For further product information, please contact Chat Support**